Study of ozone reactor with dielectric barrier discharge plasma (BDBP): variations of inner electrode based on Stainless steel, Galvalume, and Copper
Suraidin1, M. Nur2.4*, Gunawan3.4, Ade Ika Susan1
1) Magister of Physics, Faculty of Science and Mathematics, Diponegoro University,
Jl. Prof. H. Soedarto, SH, Tembalang. Semarang. INDONESIA,
2) Department of Physics, Faculty of Science and Mathematics, Diponegoro University,
3) Department of Chemistry, Faculty of Science and Mathematics, Diponegoro University,
4) Center for Plasma Research, Science and Mathematics Faculty, Diponegoro University,
Jl. Prof. H. Soedarto, SH, Tembalang. Semarang. INDONESIA.
correspondence author E-mail: m.nur@undip.ac.id
Abstract: The research of ozone reactor with dielectric barrier discharge plasma (BDBP) with variations of inner electrode based on stainless steel, galvalume, and copper has been done. The ozone was produced with oxygen as inputted gas. The ozone concentration has determined with
variations of voltage (from 3 to 5 kV) and flow rate (i.e. 2,3,4,5,6,8 and 10 L/min). Ozone reactor, has a frame with cylinder-cylinder configuration. Inner electrode (cylindrical) made of stainless steel, galvalume and copper. The three of materials was used for evaluates the inner electrode’s
corrosion resistance characteristics for DBDP reactor. The outer electrodes (cylindrical) made of zinc plate, while Pyrex used as dielectric material. AC High Voltage was used as power supply with frequency of 16 kHz. This research has been conducted with five variations of reactor’s
length of 5, 10, 15, 20, and 25 cm. The ozone concentration has measured with KI solution and then titrated using sodium thiosulphate. After used as the inner materials of ozone reactor, the corrosion test has been conducted with SEM and EDX analysis. The results showed that ozone
concentration was increasing by the increasing of voltage, and the greater gas flow rate gives the less ozone concentration. In addition, the most corrosion electrodes is one made of copper, which supported by SEM EDX result, that has CuO concentration of 60,77%. Otherwise, from
the three of materials, stainless steel is obtained as the most stainless material.
More information : Journal of Physics: Conference Series